AiZir Flash
Speed Sintering Zirconia
[ Introduction ]
Aizir Flash is a fast-firing zirconia material that can be sintered in 30 minutes while maintaining high aesthetics and strength. Its unique powder and production process can realize the same performance of fast-firing and slow-firing, and the translucency can reach 48% in both cases. High flexural strength meets the full range of end indications.
>Product Brochure[ Product Advantage ]
Flexural strength 1250MPa
AiZir Flash as a high-speed sintering zirconia material with flexural strength of 1250MPa
Multiple sintering options
Normal sintering, fast sintering and high-speed sintering can be all achieved, even with other sintering furnaces on the market.
30 min sintering for single crowns
It takes only 30 min of sintering for zirconia single crowns with no more than 3mm thickness.
Stable sintering property
The same aesthetic effect are presented at high temperature and with a wide temperature range.
[ Recommended Indications ]
Inlay/Onlay
Anterior full crown
Anterior full crown bridge
Anterior coping Anterior reduced crown
Anterior coping bridge Anteriorreduced crown bridge
Posterior full crown
Posterior full crown bridge
Posterior coping Posterior reduced crown
Posterior coping bridge Posterior reduced crown bridge
Screw-retained bridge
[ Multiple sintering options ]
Sintering | Conventional Sintering | Rapid Sintering |
Sintering time (min) | 690 | 30 |
Sintering temperature(°C) | 1530 | 1550 |
Light transmittance(%) | 48 | 48 |
Flexural strength(MPa) | 1270 | 1256 |
[ Shade and dimension ]
[ Parameters and application systems ]
Color | Vita 16 colors/OM1/OM2/OM3 |
Light transmittance(%) | 48 |
Final firing density(g/cm3) | 6.07 |
Flexural strength (MPa) | 1250 |
Fracture toughness (MPam0.5) | 6.5 |
Vickers hardness (HV10) | 1310 |
98mm
95mm
92X75mm
Block
Other
[ Digital work flow ]
Ai Flash materials represent Aidite's years of experience in digital processing, and we have validated the workflow of materials and equipment throughout the entire process, from the initial intraoral scan to the final restoration. The result is less labor involved, more efficient processing, better shipments, and Aidite's prompt, quality, and efficient service system.
[ Case ]
This trademarks of Aidite (Qinhuangdao) Technology Co., Ltd. or its affiliated companies have been registered in China and the other countries.
No unauthorized use, plagiarism or imitation, or use of unauthorized products or their business activities, shall be permitted.
Aidite (Qinhuangdao) Technology Co., Ltd. ,All Rights Reserved, 2007 -2022 Privacy Policy
Email us
Demand
Online
Demand for product upgrades
Suggestions for Aidite marketing*
Demand for New product R&D
Suggestions for Aidite service