CAD/CAM specialized temporary restoration material, composed of 99% polymethylmethacrylate (PMMA). With outstanding mechanical and compliance properties, structural and shade stability, Mono
PMMA can deliver authentic teeth like gloss, translucency, and esthetically vivid restoration.
| Bending Strength | ≥120MPa | Thickness | 12/14/16/18/20/22/25/30 |
| System | Wieland/Amann/Zirkon /Sirona | Shade | Vita 16 shades/OM1/OM2/OM3 |
| Water Sorption | ≤25[μg/mm3] | Solubility | ≤5[μg/mm3] |
CAD/CAM Anterior esthetic temporary restoration material, with revolutionary shade gradience technology, demarcation of shades realization, Multi-layer PMMA satisfies shade gradience from incisal to bottom. Excellent performance, stability, translucency and good bio-compatibility, multi-layer PMMA delivers no-stimulus features to the oral tissues.
| Bending Strength | ≥120MPa | Thickness | 12/14/16/18/20/22/25/30 |
| System | Wieland/Amann/Zirkon/Sirona | Shade | Vita 16 shades/OM1/OM2/OM3 |
| Water Sorption | ≤25[μg/mm3] | Solubility | ≤5[μg/mm3] |
Made of 100% organic materials, it is mainly suitable for the manufacture of occlusal splints and other dental instruments. It is also mostly used for cutting models and also used for metal or metal precision.
The basic die-casting application of casting mold manufacturing. The cutting is easy to cut, the filling is accurate and stable, there is no residue after it is burned out at 500 ℃; it can be expanded with cold polymer materials and can be heated Solid repair; colorless and has a very high light transmittance, a wide range of clinical applications.
| Bending Strength | ≥120MPa | Thickness | 12/14/16/18/20/22/25/28/30 |
| System | Wieland/Amann/Zirkon/Sirona/Kava | Burning Residual Monomer | 0.0%（2h，500℃） |
| Water Sorption | ≤25[μg/mm3] | Solubility | ≤1.3[μg/mm3] |
| Vickers Hardness | ≥25HV1 |
CAD/CAM denture base material, providing dental laboratories with an efficient option for making dentures. High degree of polymerization result in fewer monomer residue, less water absorption and dissolution. In addition, bionic fibers added to the material give the denture base a superior aesthetic.
| Bending Strength | ≥120MPa | Thickness | 20/22/25/30 |
| System | Wieland/Amann/Zirkon/Sirona | Shade | P1/P2/P3 |
| Water Sorption | ≤25[μg/mm3] | Residual Momomer | ≤0.50% |