Aizir Flash is a fast-firing zirconia material that can be sintered in 30 minutes while maintaining high aesthetics and strength. Its unique powder and production process can realize the same performance of fast-firing and slow-firing, and the translucency can reach 48% in both cases. High flexural strength meets the full range of end indications.
| Coefficient of thermal expansion(CTE 25-500℃) | (10.5±0.5)×10-6K-1 |
| Chemical solubility | ≤100μm.cm-2 |
| Fracture toughness | ≥5MPam0.5 |
| Sintered density | ≥6.0g/cm3 |
| Vickers hardness | ≥1250HV10 |
Sintering | Conventional Sintering | Rapid Sintering |
Sintering time (min) | 690 | 30 |
Sintering temperature(°C) | 1530 | 1550 |
Light transmittance(%) | 48 | 48 |
Flexural strength(MPa) | 1270 | 1256 |
Flexural strength 1250MPa
AiZir Flash as a high-speed sintering zirconia material with flexural strength of 1250MPa
Multiple sintering options
Normal sintering, fast sintering and high-speed sintering can be all achieved, even with other sintering furnaces on the market.
30 min sintering for single crowns
It takes only 30 min of sintering for zirconia single crowns with no more than 3mm thickness.
Stable sintering property
The same aesthetic effect are presented at high temperature and with a wide temperature range.
Ai Flash materials represent Aidite's years of experience in digital processing, and we have validated the workflow of materials and equipment throughout the entire process, from the initial intraoral scan to the final restoration. The result is less labor involved, more efficient processing, better shipments, and Aidite's prompt, quality, and efficient service system.