3D Pro zir is fabricated with the most advanced production processes at Aidite, producing a layerless,natural shade gradient, with optimal strengthand translucency, transitioning from Cervical to Incisal areas of the restoration. With a maximum flexural strength of 1100 MPa, 3D Pro zirensures aesthetic results while being suitable for all indications from single crowns to 14-unitbridge structures.
| Coefficient of thermal expansion(CTE 25-500℃) | (10±0.5)×10-6K-1 |
| Chemical solubility | ≤100μm.cm-2 |
Fracture toughness | ≥5MPam0.5 |
| Sintered density | ≥6.0g/cm³ |
| Vickers hardness | ≥6.0g/cm³ |
Bionic
3D pro Zir is developed by Aidite Technology and Peking University School of Stomatology. The material comes closer to natural teeth. Not only from the esthetic point of view, also its abrasion characteristics makes it to a dental material with biomimetic properties.
High Strength
The flexural strength of 3D pro zir is up to 1100 MPa which is greatly improved. Long span bridges are stable and fully meet the strength requirements of laboratories for a broad range of indications.
Layerless Natural Transition
Matching the color transition of natural teeth from cervical to incisal, 3D pro zir has a smooth color gradient without visible layer.
Fast Delivery
3D pro zir is the leading digital solution in the field of zirconia materials. The excellent characteristics of the material itself, combined with the 3D pro zir Rapid Aesthetic Solution will help laboratories to finalize and deliver zirconia restorations within 24 hours.
3D Pro zir is available in 16 shades of the classical VITA shade guide and 3 bleach shades OM1/OM2/OM3. For individual further charac-terisation, Biomic Stain&Glaze can be used. 3D Pro zir simplifies the whole process in achieving highly aesthetic results.